Zinc oxide desulfurization Catalysts Series

Wide-Temperature Zinc Oxide Fine Desulfurization Catalyst

Wide-Temperature Zinc Oxide Fine Desulfurization Catalyst has widely been used to remove H2S from feed gases in production of hydrogen, methanol, ammonia, fine chemicals (DMF, TDI, MDI, H2O2,etc.),etc.


Inquire Now
Product Description

Wide-Temperature Zinc Oxide Fine Desulfurization Catalyst  

Product Description

ShapeExtrusions
Dimensions ( mm )Φ3-5×3--20
Bulk Density1.0~1.2kg/L
Crushing Strength, N/cm≥ 40N/cm
Zinc Oxide Content(or Zinc as ZnO)
≥80% or as per requirement
H2S capacity,%min10(30-100°C)
min20(220°C)
min30(350°C)


Benefits  

High sulfur capacity at a wide temperature range, from ambient temperature to above 400°C; 

Capable of converting and absorbing simple organic sulfur such as COS and CS2;    

High strength with good water-resistance quality.   